●产品名称：保证淬透性结构钢
Structural steels with specified hardenability bands
●钢号：SCM440H
Steel grade：SCM440H
●执行标准：JIS G4052-2003
Execution standard：JIS G4052-2003
●钢组系列：CrMo
Steel series：CrMo
●钢厂：石钢、冶钢、东北特钢等。
Steel: steel, metallurgical steel, northeast special steel, etc.
●交货状态：一般以退火状态交货，具体交货状态应在质保书中注明。
Delivery status: general with annealing state delivery, delivery status should be indicated in the warranty.

●SCM440H化学成份范围值:
注：实际化学成分以钢厂质保书为准。
SCM440HChemical composition range value:
Note: the actual chemical composition of the steel factory warranty shall prevail.
C:0.37~0.44
Si：0.15~0.35
Mn：0.55~0.95
P：≤0.030
S：≤0.030
Cr：0.85~1.25
Mo：0.15~0.35
Ni：≤0.25
Cu：≤0.30

●SCM440H力学性能范围值:
注：实际力学性能以钢厂质保书为准。
抗拉强度σb(MPa)：≥1080 　
屈服强度σs(MPa)：≥930　
伸长率δ5(%)：≥12 　
断面收缩率ψ(%)：≥45 　
冲击功Akv(J)：≥63 　
冲击韧性值αkv(J/cm2)：≥78 　
硬度：≤217HB 　
Tensile strength of sigma b (MPa) :≥1080
Yield strength sigma s (MPa) : ≥930　
Elongation delta (%) : 12 　
Reduction of area bits (%) : ≥45
Impact energy Akv (J) : ≥63
Impact toughness values of alpha kv (J/cm2) : ≥78
Hardness:≤217HB 　

●SCM440H用途举例：
用于制造比35CrMo钢要求强度更高或截面尺寸更大的重要零件，如机车牵引用大齿轮、增压器传动齿轮、后轴、变速箱齿轮、发动机气缸、SCM440H受载荷极大的连杆、弹簧夹，以及用于1200-2000mm石油深井的钻杆接头与打捞工具等。
SCM440H purposes, for example:
Used in the manufacture of higher than 35 crmo steel demand intensity or section size more important parts, such as locomotive traction with the big gear, the supercharger drive gear, rear axle, transmission gear, engine cylinder, SCM440H load of connecting rod, a spring clip, as well as for 1200-2000 - mm deep well of oil drill pipe joint and the fishing tools, etc.

●SCM440H性能特点：
与SCM435H钢的性能相近，由于碳和铬含量增高，因而其强度和淬透性均优于SCM435H钢，SCM440H调质后具有较高的疲劳强度和抗多次冲击能力，低温冲击韧度良好，无明显的回火脆性，SCM440H一般在调质后使用，可代替含镍较高的调质钢。
SCM440H performance characteristics:
Close to the performance of SCM435H steel, as a result of carbon and chromium content is higher, so its strength and hardenability were better than SCM435H steel, after SCM440H conditioning has high fatigue strength and the repeated impact resistance, low temperature impact toughness is good, no obvious temper brittleness, SCM440H in commonly used after quenched and tempered, nickel high quenched and tempered steel can be substituted.